YJS-601 carbon fiber impregnated plastic Contact: Zhang Ruihua: 15838079336 YJS-601 carbon fiber impregnated plastic solvent-modified epoxy resin adhesive. Group A were: B = 3:1. ★ Uses mainly used for paste carbon fiber. The goods on the carbon fiber having a strong permeability, high tensile bond strength and connection strength; wear-resistant anti-corrosion, high durability and excellent mechanical properties. Technical indicators: technical indicators meet the GB50367-2006 standard requirements. Performance requirements of the test results of the performance of the project (A) colloidal properties of tensile strength (MPa) 43.4 ≥ 40 elasticity modulus (MPa) 2527 ≥ 2500 elongation rate (%) 1.86 ≥ 1.5 Compressive strength (MPa) 74.5 ≥ 70 flexural strength (MPa) 53.3 ≥ 50, and shall not be brittle (cataclastic) destroy the bonding capacity of steel - steel tensile shear strength standard value (Mpa) 14.6 ≥ 14 with concrete positive pull, bond strength (Mpa) 3.24, and cohesive failure in the concrete ≥ 2.5, and poly undermine ★ use methods and precautions for the concrete, the YJS-601 carbon fiber impregnated plastic mixed 3:1 ratio of Part A and Part B, Stir that may be used. 2, mixed YJS-601 glue should be finished within 60 ~ 90min (depending on the ambient temperature). 3, the density of the goods from about 1.15 to 1.25g/cm3 (cured product), the gel time of about 3 to 6 hours. ★ storage and transport, the product can be stored in a 40 ° C below ambient temperature, shelf life of 24 months. 2, the product is a solvent-based, and should be stored away from open flame heating device. ★ Packaging Specifications: 9kg +3 kg / group ★ bonded carbon fiber reinforced construction on construction conditions: (1) The construction of the surface should be clean and dry. (2) Construction of the temperature should be greater than 15 ℃, less than 40 ° C (3) non-rainy day open-air construction. (4) relative to the temperature is greater than 85% or concrete surface exposed to the case, does not allow construction. Construction Technology: primary requirements: bonding surface must be flat, solid, free of impurities, repair glue has hardened, and the surface is dry, there is no dew, frost. 2, the gel: calculated in accordance with the bond area usage, accurately weighed, and Part B, in full uniform mixing in a clean container. Good tune glue should be used in the applicable period. Brushing the bottom glue: uniform YJS-602 carbon fiber bottom gum mixed pro rata brushing directly to the concrete base, concrete surface with glue full. Hardening after the next process. 4, paste carbon fiber: ① with a stiff brush will tuned YJS-601 impregnated glue evenly brushing to the bonding surface, the glue full amount must be sufficient. The brushing was about 600-800g/m2. ② will cut carbon fiber the fiber sheet affixed to the surface of concrete paste, hard rubber stick or plastic scraper reciprocating RCC, to procure carbon fiber straight to extend full penetration of the adhesive. Carbon fiber cloth long upward joints take the length of 10-20 mm. ③ part adhesive brushing the surface of the carbon fiber continue reciprocating Scratch RCC, driven out of bubbles, and the adhesive is evenly covering the carbon fiber cloth. The Brushing approximately 200g / ㎡. ④ allowed to stand for 1-2 hours to refers to dry, repeat RCC eliminate the bubbles may be caused due to the floatation of carbon fibers or shifted, adhesive untrue. The ⑤ multilayer sticky, you can repeat the above operation. ⑥ adhesive is cured after being pasted on the surface of the carbon fiber, then knife coating a layer of glue. Note: 1, with plastic proper ventilation. 2, the operator uses a safety mirror, wearing a protective mask. Rain, frost and fog weather may not outdoor construction. 4, carbon fiber is conductive fiber construction operation must be kept away from the power supply to avoid electric shock casualties. Outdoors near a charged body (wire) construction, if the wind should stop construction, in order to avoid carbon fiber cloth wind blowing contact conductor accident. 5, carbon fiber cloth fiber direction for a single direction, unit weight, thickness, tensile strength, elastic modulus indicators must comply with the relevant requirements. YJS-602 carbon fiber bottom plastic Usage: mainly used to paste on the surface of the concrete structure reinforced carbon fiber front can penetrate the surface of the inner layer to improve the soft and the overall force effects of the concrete surface and the CFRP. Technical indicators: technical indicators meet the GB50367-2006 standard requirements. Performance requirements of the test results of the performance of the project (rubber match with Class A) bonding capacity of steel - steel standard values ??of tensile shear strength (Mpa) 15.0 ≥ 14 with concrete positive pull, bond strength (MPa) 3.27 for concrete poly destruction of ≥ 2.5, and for cohesive failure within the concrete using methods and precautions: 1, Part A and Part B of the YJS-602 carbon fiber bottom glue mixed 3:1 ratio, stir, can be used. 2, mixed YJS-602 glue should be finished within 60 ~ 90min (depending on the ambient temperature). 3, the density of the goods from about 1.15 to 1.25g/cm3 (cured product), the gel time of about 3 to 6 hours. Storage and transport: 1, the product can be stored in a 40 ° C below ambient temperature, shelf life of 24 months. Product solvents should be stored away from open flame, heating devices, packaging specifications: The product is packaged 9kg +3 kg / group. YJS-603 leveling adhesive product uses carbon fiber is mainly used for the fill level of CFRP and the concrete structure of the surface of base. The high viscosity putty-like, strong bonding, resistance to alternating load performance is excellent, with excellent mechanical properties, good toughness, wear-resistant, corrosion resistant, waterproof. Technical indicators technical indicators meet the GB50367-2006 standard requirements. Performance requirements of the test results of the performance of the project (rubber match with Class A) colloidal properties of colloidal tensile strength (MPa) 32.4 ≥ 30 colloidal flexural strength (Mpa) 40.6 ≥ 40 and may not be destruction and concrete was brittle (cataclastic) is pulling bonding strength (Mpa) 3.03, and concrete cohesive failure ≥ 2.5, and undermine the use of methods and precautions for concrete poly YJS-603 leveling adhesive A and B will produce precipitation during storage and transport before use hand electric drill respectively Stir. Leveling adhesive, YJS-603 Part A: B = 3:1 ratio mixing evenly. 3, the product density of 1.40 ~ 1.60g/cm3 (cured), mixed use time about 30 ~ 60min (depending on the ambient temperature). The gel time of about 1.5 to 3 hours. Packaging storage: 1, the product can be stored in a 40 ° C below ambient temperature, shelf life of 24 months. 2, the product is a solvent-based, and should be stored away from open flame heating device. 3, the product packaging 15kg +5 kg / group. Construction conditions: 1, construction of the surface should be clean and dry. Construction temperature should be greater than 15 ℃, less than 40 ° C., is strictly prohibited in the rainy day open-air construction. 4, the relative temperature is greater than 85% or concrete surface condensation occasions, do not allow the construction. Construction Technology: primary requirements: bonding surface must be flat, solid, free of impurities, repair glue has hardened, and the surface is dry, there is no dew, frost. 2, the gel: calculated in accordance with the bond area usage, accurately weighed, and Part B, in full uniform mixing in a clean container. Good tune glue should be used in the applicable period. Brushing the bottom glue: uniform YJS-602 carbon fiber bottom gum mixed pro rata brushing directly to the concrete base, concrete surface with glue full. Hardening after the next process. 4, paste carbon fiber: ① with a stiff brush will tuned YJS-601 impregnated glue evenly brushing to the bonding surface, the amount of plastic must be adequate and full. Brushing approximately 400-600g/m2. ② will cut carbon fiber the fiber sheet affixed to the surface of concrete paste, hard rubber stick or plastic scraper reciprocating RCC, to procure carbon fiber straight to extend full penetration of the adhesive. Carbon fiber cloth length up joints take the length should be 10-20 mm. ③ part adhesive brushing the surface of the carbon fiber continue reciprocating Scratch RCC, driven out of bubbles, and the adhesive is evenly cover the carbon fiber cloth. The Brushing approximately 200g / ㎡. ④ allowed to stand for 1-2 hours to refers to dry, repeat RCC eliminate the bubbles may be caused due to the floatation of carbon fibers or shifted, adhesive untrue. The ⑤ multilayer sticky, you can repeat the above operation. ⑥ adhesive is cured after being pasted on the surface of the carbon fiber, then knife coating a layer of glue. Note: 1, with plastic proper ventilation. 2, the operator uses a safety mirror, wearing a protective mask. Rain, frost and fog weather may not outdoor construction. 4, carbon fiber is conductive fiber construction operation must be kept away from the power supply to avoid electric shock casualties. Outdoors near a charged body (wire) construction, if the wind should stop construction, in order to avoid carbon fiber cloth wind blowing contact conductor accident. 5, carbon fiber cloth fiber direction for a single direction, unit weight, thickness, tensile strength, elastic modulus indicators must comply with the relevant requirements. Contact: Zhang Ruihua: 15838079336